Abstract
INTRODUCTION: Bond failure during fixed orthodontic treatment is a frequently occurring problem. As bracket rebonding is associated with reduced shear bond strength, the aim of the present investigation is to analyse the effect of different innovative rebonding systems to identify optimised rebonding protocols for orthodontic patient care. METHODS: Metallic brackets were bonded to the frontal enamel surfaces of 240 bovine lower incisors embedded in resin bases. Teeth were randomly divided into two major experimental groups: in group 1 a hydrophilic primer (Assure™ PLUS) was compared to commonly used orthodontic adhesives (Transbond XT™, BrackFix®, Grengloo™) and a zero control. In group 2 different rebonding systems were analysed using a hydrophilic primer (Assure™ PLUS), a methyl methacrylate-consisting primer (Plastic Conditioner) and a conventional adhesive (Transbond XT™). All teeth were tested for shear bond strength according to the DIN-13990 standard, the Adhesive Remnant Index and enamel fracture rate. RESULTS: The hydrophilic primer enhanced shear bond strength at first bonding (Assure™ PLUS 20.29 ± 4.95 MPa vs. Transbond XT™ 18.45 ± 2.57 MPa; BrackFix® 17 ± 5.2 MPa; Grengloo™ 19.08 ± 3.19 MPa; Meron 8.7 ± 3.9 MPa) and second bonding (Assure™ PLUS 16.76 ± 3.71 MPa vs. Transbond XT™ 13.06 ± 3.19 MPa). Using Plastic Conditioner did not seem to improve shear bond strength at rebonding (13.57 ± 2.94). When enamel etching was left out, required shear bond strength could not be achieved (Plastic Conditioner + Assure™ PLUS 8.12 ± 3.34 MPa; Plastic Conditioner: 3.7 ± 1.95 MPa). Hydrophilic priming systems showed decreased ARI-scores (second bonding: 2.63) and increased enamel fracture rates (first bonding: 55%; second bonding 21,05%). CONCLUSIONS: Based on the present study we found that rebonding strength could be compensated by the use of hydrophilic priming systems. The additional use of a methyl methacrylate-consisting primer does not seem to enhance shear bond strength. No etching approaches resulted in non-sufficient bond strength.