Abstract
The effect of Fe2O3 crystal phases on their performance in CO2 hydrogenation was studied. α-Fe2O3 crystal was prepared by precipitation method from Fe(NO3)3·9H2O and (NH4)2CO3, and γ-Fe2O3 was prepared by grinding Fe(NO3)3·9H2O and L(+)-Tartaric acid in agate mortar completely. The crystal phases of Fe2O3 influence the distribution of promoter Zn, K and Cu on catalysts. The dispersity of K on γ-Fe2O3 surface is higher than α-Fe2O3. On the contrary, Cu and Zn are more dispersive on α-Fe2O3 surface than γ-Fe2O3. The catalyst in γ-Fe2O3 phase is easily reduced relative to the catalyst in α-Fe2O3 phase. The former presents higher CO2 conversion and C2+ hydrocarbon selectivity than the latter in CO2 hydrogenation.