Abstract
Mixed-matrix membranes (MMMs) were developed by impregnating organofunctionalized nanoadditives within fouling-susceptible polysulfone matrix following the non-solvent induced phase separation (NIPS) method. The facile functionalization of nanoparticles of anatase TiO2 (nano-TiO2) by using two different organoligands, viz. Tiron and chromotropic acid, was carried out to obtain organofunctionalized nanoadditives, FT-nano-TiO2 and FC-nano-TiO2, respectively. The structural features of nanoadditives were evaluated by X-ray diffraction, X-ray photoelectron spectroscopy, Raman and Fourier transform infrared spectroscopy, which established that Tiron leads to the blending of chelating and bridging bidentate geometries for FT-nano-TiO2, whereas chromotropic acid produces bridging bidentate as well as monodentate geometries for FC-nano-TiO2. The surface chemistry of the studied membranes, polysulfone (Psf): FT-nano-TiO2 UF and Psf: FC-nano-TiO2 UF, was profoundly influenced by the benign distributions of the nanoadditives enriched with distinctly charged sites ([Formula: see text]), as evidenced by superior morphology, improved topography, enhanced surface hydrophilicity and altered electrokinetic features. The membranes exhibited enhanced solvent throughputs, viz. 3500-4000 and 3400-4300 LMD at 1 bar of transmembrane pressure, without significant compromise in their rejection attributes. The flux recovery ratios and fouling resistive behaviours of MMMs towards bovine serum albumin indicated that the nanoadditives could impart stable and appreciable antifouling activity, potentially aiding in a sustainable ultrafiltration performance.