Background
Calcium silicate-based cements are biomaterials with calcium oxide and carbonate filler additives. Their properties are close to those of dentin, making them useful in restorative dentistry and endodontics. The
Conclusion
These two biomaterials both seem to be bioactive and biocompatible, preserving DPSC proliferation, migration and adhesion. The observed strong mineralization induction through direct contact highlights the potential of these biomaterials for clinical application in dentin-pulp complex regeneration.
Results
The two biomaterials were compared and did not modify dental pulp stem cell (DPSC) proliferation. BD and BR showed no significant cytotoxicity, although some cell death occurred in direct contact. No apoptosis or inflammation induction was detected. A striking increase of mineralization induction was observed in the presence of BD and BR, and this effect was greater in direct contact. Surprisingly, biomineralization occurred even in the absence of mineralization medium. This differentiation was accompanied by expression of odontoblast-associated genes. Exposure by indirect contact did not stimulate the induction to such a level.