Abstract
Boron nitride, also known as white graphene, has attracted extensive attention in the fields of adsorption, catalysis and hydrogen storage due to its excellent chemical properties. In this study, a phosphorus-doped boron nitride (P-BN) material was successfully prepared using red phosphorus as a dopant for the preparation of porous boron nitride precursors. The phosphorus content in the P-BN was adjusted based on the addition rate of phosphorus. The specific surface area of P-BN first increased and then decreased with increasing addition rate of phosphorus. The maximum specific surface area was 837.8 m(2) g(-1) when the phosphorus addition rate was 0.50. The P-BN prepared in the experiments was used as an adsorbent, and its adsorption capacity for heavy metals from flue gas was investigated. In particular, P-BN presented a stronger adsorption selectivity for zinc compared with other heavy metals, and its adsorption capacity for zinc was 5-38 times higher than for other heavy metals. The maximum adsorption capacity of P-BN for zinc and copper in a single heavy metal atmosphere was 69.45 and 53.80 mg g(-1), respectively.