Abstract
Ceramic membranes have been widely used in oil-water treatment; however, membrane fouling remains a challenge that must be addressed to improve the process feasibility. A thin layer of polydopamine (PDA) was dynamically deposited on the surface of the alumina hollow fiber membranes to reduce oil adhesion. The PDA-alumina membranes were characterized by using SEM-EDS, AFM, and water contact angle measurements. The performance of the modified membranes was evaluated using synthetic crude oil emulsions (100 mg·L(-1)) in a crossflow system. Membranes modified with PDA exhibited 97% oil rejection, and a stabilized permeate flux of 463 L·h(-1)·m(-2) with a relative flux reduction of 60% and a flux recovery ratio of 75% was observed after cleaning, indicating lower oil adhesion and better fouling reversibility. The most predominant fouling mechanism for the modified membranes seems to be cake filtration because of the reduction in pore size due to the deposition of the PDA layer.