Abstract
In this study, we present a novel and straightforward approach for the synthesis of copolymers and nanocomposites based on α- and β-pinene, employing an eco-friendly and cost-effective nano-reinforcing filler. The copolymers (α-co-β-P) were produced through cationic copolymerization, using AlCl(3) as a catalyst. The structural characterization of the resulting copolymer was validated through FT-IR, (1)H-NMR spectroscopy, and differential scanning calorimetry (DSC). The molecular weight of the obtained polymer is determined by Gel Permeation Chromatography (GPC) analysis and is about 4500 g/mol. Nanocomposites (α-co-β-P/Clay 2, 5, 8, and 10% by weight of nano-clay) were synthesized by combining clay and α-co-β-P copolymer in solution using ultrasonic irradiation. This ultrasound-assisted method was employed to enhance and assess the structural, morphological, and thermal properties of the pure copolymer. The morphology of the resultant nanocomposites was characterized using infrared spectroscopy (FT-IR), X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Thermogravimetric analysis (TGA) revealed that the nanocomposites exhibit a higher degradation temperature compared to the pure copolymer. The analyses provided evidence of the chemical modification of nano-clay layers and their uniform dispersion in the α-co-β-P copolymer matrix. Exfoliated structures were achieved for lower clay concentration (2% by weight), while intercalated structures and immiscible regions were observed for higher clay concentrations (5, 8, and 10% by weight). The antioxidant activity of α-pinene, β-pinene, and the obtained nanocomposites were studied using DPPH (2,2-diphenyl-1-picrylhydrazyl) as a model free-radical. The results demonstrate a significant antioxidant potential of the nanocomposites, showcasing their ability to effectively neutralize free-radicals. Finally, a novel procedure was devised for the rapid synthesis of copolymers and nanocomposites using α- and β-pinene.