Abstract
In this study, ternary Cu₂SnS₃ (CTS) nanostructure materials with high crystallinity were successfully prepared via a facile solvothermal method, which was followed by high-temperature treatment. The morphology of the as-synthesized samples is uniform flower-like spheres, with these spheres consisting of hierarchical nanosheets and possessing network features. Sodium storage measurements demonstrate that the annealed CTS electrodes have high initial reversible capacity (447.7 mAh·g(−1) at a current density of 100 mA·g(−1)), good capacity retention (200.6 mAh·g(−1) after 50 cycles at a current density of 100 mA·g(−1)) and considerable rate capability because of their high crystallinity and unique morphology. Such good performances indicate that the high crystallinity CTS is a promising anode material for sodium ion batteries.