Abstract
NaNiO(2) is a layered material consisting of alternating layers of NaO(6) and Jahn-Teller-active NiO(6) edge-sharing octahedra. At ambient pressure, it undergoes a broad phase transition from a monoclinic to rhombohedral structure between 465 and 495 K, associated with the loss of long-range orbital ordering. In this work, we present the results of a neutron powder diffraction study on powdered NaNiO(2) as a function of pressure and temperature from ambient pressure to ∼5 GPa between 290 and 490 K. The 290 and 460 K isothermal compressions remained in the monoclinic phase up to the maximum pressures studied, whereas the 490 K isotherm was mixed-phase throughout. The unit-cell volume was fitted to a second-order Birch-Murnaghan equation of state, where B = 119.6(5) GPa at 290 K. We observe at 490 K that the fraction of the Jahn-Teller-distorted phase increases with pressure, from 67.8(6)% at 0.71(2) GPa to 80.2(9)% at 4.20(6) GPa. Using this observation, in conjunction with neutron diffraction measurements at 490 K on removing pressure from 5.46(9) to 0.342(13) GPa, we show that the Jahn-Teller transition temperature increases with pressure. Our results are used to present a structural pressure-temperature phase diagram for NaNiO(2). To the best of our knowledge, this is the first diffraction study of the effect of pressure on the Jahn-Teller transition temperature in materials with edge-sharing Jahn-Teller-distorted octahedra and the first variable-pressure study focusing on the Jahn-Teller distortion in a nickelate.