Abstract
A bio-inspired nanofibrous MnO2-TiO2-carbon composite was prepared by utilizing natural cellulosic substances (e.g., ordinary quantitative ashless filter paper) as both the carbon source and structural matrix. Mesoporous MnO2 nanosheets were densely immobilized on an ultrathin titania film precoated with cellulose-derived carbon nanofibers, which gave a hierarchical MnO2-TiO2-carbon nanoarchitecture and exhibited excellent electrochemical performances when used as an anodic material for lithium-ion batteries. The MnO2-TiO2-carbon composite with a MnO2 content of 47.28 wt % exhibited a specific discharge capacity of 677 mAh g-1 after 130 repeated charge/discharge cycles at a current rate of 100 mA g-1. The contribution percentage of MnO2 in the composite material is equivalent to 95.1% of the theoretical capacity of MnO2 (1230 mAh g-1). The ultrathin TiO2 precoating layer with a thickness ca. 2 nm acts as a crucial interlayer that facilitates the growth of well-organized MnO2 nanosheets onto the surface of the titania-carbon nanofibers. Due to the interweaved network structures of the carbon nanofibers and the increased content of the immobilized MnO2, the exfoliation and aggregation, as well as the large volume change of the MnO2 nanosheets, are significantly inhibited; thus, the MnO2-TiO2-carbon electrodes displayed outstanding cycling performance and a reversible rate capability during the Li+ insertion/extraction processes.