Abstract
Martensitic stainless steel (MSS) is widely used in several parts of automobiles where high strength, hardness, and corrosion resistance are required. However, the metastability of retained austenite can transform into martensite under severe deformation, adversely affecting material properties. Cryogenic treatments (CTs) have been extensively employed in iron-based alloys for fastener application due to their advantageous effect. This study explores the heat treatment processes applied to 13Cr-2Ni-2Mo martensitic stainless steel (MSS), including austenitizing, cryogenic treatment, and tempering cycles. Cryogenic treatment at (-150 °C) for varying durations, followed by tempering at 200 °C for 2 h, and the impact of post-cryogenic tempering at 200 °C for different tempering duration on the microstructure and mechanical properties were evaluated. Experimental results indicate that the sample quenched at 1040 °C for 2 h (CHT) contains lath martensite, retained austenite, δ-ferrite, and undissolved carbide precipitation. Compared to as-quenched samples, hardness decreased by 5.04%, 7.24%, and 7.32% after tempering for 2 h, 5 h, and 10 h, respectively. Extending cryogenic durations to 2 h, 12 h, and 20 h promoted nucleation of a mixture of M(3)C and M(23)C(6) small globular carbides (SGCs) and grain refinement but resulted in hardness reductions of 5.04%, 5.32%, and 8.36%, respectively. The reduction in hardness is primarily attributed to a decrease in solid solution strengthening and promoted carbide coarsening.