Abstract
This study evaluated the surface functionalization of a non-equiatomic TiZrNbTaMo high-entropy alloy (HEA) by micro-arc oxidation (MAO) in Cu-rich electrolytes to tailor its performance for biomedical implants. The Cu content was varied, and the resulting coatings were investigated for their morphology, phase constitution, chemical structure, wettability, and cytocompatibility. X-ray diffraction (XRD) measurements of the substrate indicated a body-centered cubic (BCC) matrix with minor HCP features, while the MAO-treated samples depicted amorphous halo with sparse reflections assignable to CaCO(3), CaO, and CaPO(4). Chemical spectroscopic analyses identified the presence of stable oxides (TiO(2), ZrO(2), Nb(2)O(5), Ta(2)O(5), MoO(3)) and the successful incorporation of bioactive elements (Ca, P, Mg) together with traces of Cu, mainly as Cu(2)O. MAO treatment increased surface roughness and rendered a hydrophilic behavior, which are features typically favorable to osseointegration process. In vitro cytotoxic assays with MC3T3-E1 cells (24 h) showed that Cu addition did not induce harmful effects, maintaining or improving cell viability and adhesion compared to the controls. Collectively, MAO in Cu-rich electrolyte yielded porous, bioactive, and Cu-incorporated oxide coatings on TiZrNbTaMo HEA, preserving cytocompatibility and supporting their potential for biomedical applications like orthopedic implants and bone-fixation devices.