Abstract
At present, the design and fabrication of polymer membranes with high permeability and good retention ability are still huge challenges. In this study, the commercial Poloxamer 407 (Pluronic F127) is selected as a multifunctional additive, and polyvinylpyrrolidone is used as a pore-forming agent to modify the poly(ether sulfone) membrane by liquid-liquid phase conversion technology to prepare an ultrafiltration membrane with excellent performance. The hydrophobic poly(propylene oxide) segment in Poloxamer 407 guarantees that this copolymer can be firmly anchored to the poly(ether sulfone) matrix, and the hydrophilic poly(ethylene oxide) segments in Poloxamer 407 impart a stronger hydrophilic nature to the modified membrane surface. Therefore, the permeability and hydrophilicity of the modified membrane are significantly improved and the modified membrane also has good stability. When the amount of Poloxamer 407 added to the casting solution reached 0.6 g, the water flux of the modified membrane was as high as 368 L m(-2) h(-1), and the rejection rate of bovine serum albumin was close to 98%. In the test to isolate organic small molecule dyes, the retention rate of the modified membrane to Congo red is 94.27%. In addition, the modified membrane shows an excellent water flux recovery rate and antifouling ability. It performs well in subsequent cycle tests and long-term membrane life tests and can be used repeatedly. Our work has resulted in poly(ether sulfone) membranes with good performance, which show great potential in the treatment of biomedical wastewater and the removal of industrial organic dye wastewater, it provides ideas for the development and application of amphiphilic polymer materials.