Abstract
The corrosion behavior of the TiTaNbZrAg alloys with different amounts of tantalum (0%, 10% and 20%) and with distinct surface topography (smooth and rough) was investigated in phosphate buffer solution (PBS) for long-time immersion (1000 h). By this approach, we expect to bring about new insights into the influence of both the amount of Ta in the alloy composition and the surface topography on the corrosion behavior of the Ti-based alloys. The corrosion resistance was studied by Open Circuit Potential (OCP), Potentiodynamic Polarization (PP), and Electrochemical Impedance Spectroscopy (EIS). From the potentiodynamic investigations, it was observed that all types of samples showed good corrosion resistance (i.e., R(corr) < 10 µm y(-1)) and may be used successfully for medical applications. However, the samples with smooth surfaces and with a certain amount of Ta (10% and 20%) exhibit the best corrosion performance (R(corr) < 1 µm y(-1)). As regards the samples with rough surfaces, the results evidenced that they showed lower corrosion resistance (1 < R(corr) < 3 µm y(-1)), suggesting that the Ta presence does not necessarily hinder the corrosion processes. Actually, the synergetic effect of both the presence of Ta and surface roughness plays an important role in corrosion resistance.