Abstract
To obtain industrialized poly(ethylene terephthalate) (PET) composites with highly efficient flame retardancy, a phosphorus-nitrogen (P-N) containing hyperbranched flame retardant additive was synthesized by 9,10-dihydro-9-oxa-10-phospho-phenanthrene-butyric acid (DDP) and tris(2-hydroxyethyl) isocyanurate (THEIC) through high temperature esterification known as hyperbranched DDP-THEIC (hbDT). The chemical structure of the synthesized hbDT was determined by FTIR, (1)H NMR, (13)C NMR, and GPC, etc. Subsequently, hbDT/PET composites were prepared by co-blending, and the effects of hbDT on the thermal stability, flame retardancy, combustion performance, and thermal degradation behavior of PET were explored to deeply analyze its flame retardant mechanism. The test results showed that hbDT was successfully synthesized, and that hbDT maintained thermal stability well with the required processing conditions of PET as retardant additives. The flame retardant efficiency of PET was clearly improved by the addition of hbDT via the synergistic flame-retardant effect of P and N elements. When the mass fraction of flame retardant was 5%, the LOI of the hbDT/PET composite increased to 30.2%, and the vertical combustion grade reached UL-94 V-0. Compared with pure PET, great decreased total heat release (decreased by 16.3%) and peak heat release rate (decreased by 54.9%) were exhibited. Finally, the flame retardant mechanism of hbDT/PET was supposed, and it was confirmed that retardant effect happened in both the gas phase and condensed phase. This study is expected to provide a new idea for the development of low toxic, environment-friendly and highly efficient flame retardant additive for polyesters in an industry scale.