Abstract
A rigid polyurethane foam (RPUF) composite was prepared by compounding phytic acid (PA)-functionalized Graphite oxide (PA-GO) with flame-retardant poly (Ammonium phosphate) (APP) and expandable graphite (EG). The effects of PA-GO on the thermal, flame-retardant, and mechanical properties of RPUF were studied using a thermogravimetric analyzer, a limiting oxygen index (LOI) tester, a UL-94 vertical combustion tester, a cone calorimeter, scanning electron microscopy, and a universal tensile testing machine. The results indicated that there was a significant synergistic flame-retardant effect between PA-GO and the intumescent flame retardants (IFR) in the RPUF matrix. Compared with RPUF-1, the addition of 0.3 wt% PA-GO could increase LOI from 25.7% to 26.5%, increase UL-94 rating from V-2 to V-0, and reduce the peak heat release rate (PHRR) and total heat release rate (THR) by 28.5% and 22.2%, respectively. Moreover, the amount of residual char increased from 22.2 wt% to 24.6 wt%, and the char layer was continuous and dense, with almost no holes. Meanwhile, the loss of mechanical properties was apparently lightened.