Abstract
The aim of this study was to evaluate the effect of an epoxy resin-based (AH-Plus), a zinc oxide eugenol containing (Pulp-Canal-Sealer) and two calcium silicate containing (MTA-Fillapex and BioRoot-RCS) sealers on primary human osteoblasts (hOB) in freshly mixed and set state. All sealers were mixed strictly according to the manufacturers´ instructions and identically samples were produced. In a pretest cytotoxic sealer concentrations were determined. Thus, for the main cell culture study, dilutions of sealer extract 1:1, 1:2, and 1:10 were used. To simulate a clinical scenario, extracts from freshly mixed sealer were added to the cells on day one. Extracts form set sealers were used for subsequent culturing for 24h, 7d, 14d, and 21d. Cell viability was analyzed by living-cell-count, MTT-assay, and living/dead-staining, cytotoxicity by LDH-assay, and changes by Richardson-staining. All data were statistically evaluated by one way ANOVA and a posthoc analysis with Bonferroni-Holm testing (p<0.05). AH-Plus was cytotoxic in a freshly mixed state, but not when the sealer was set. MTA-Fillapex and Pulp-Canal-Sealer were cytotoxic in a fresh as well as in a set state. BioRoot-RCS showed the lowest toxicity in both states; where as a regeneration of the cells could be observed over time (p<0.05). Contact of freshly mixed AH-Plus to osteoblasts should be avoided. Pulp Canal Sealer and MTA-Fillapex showed no biocompatibility in contact with osteoblasts at all. BioRoot-RCS had a positive influence on the cell metabolism (bioactivity) and is biocompatible.