Abstract
Polymer donors and non-fullerene acceptors have played an important role as photoactive materials in the development of high-efficiency organic solar cells and have immense potential in devices for direct solar hydrogen generation. However, their use in direct solar water-splitting devices has been limited by their instability in aqueous environment and recombination losses at the interface with catalysts. Here we report anodes containing PM6:D18:L8-BO photoactive layers reaching high solar water oxidation photocurrent density over 25 mA cm(-2) at +1.23 V versus reversible hydrogen electrode and days-long operational stability. This was achieved by integrating the organic photoactive layer with a graphite sheet functionalized with earth-abundant NiFeOOH water oxidation catalyst, which provides both water resistance and electrical connection between the catalyst and the photoactive layer without any losses. Using monolithic tandem anodes containing organic PM6:D18:L8-BO and PTQ10:GS-ISO photoactive layers, we achieve a solar-to-hydrogen efficiency of 5%. These results pave the way towards high-efficiency, stable and unassisted solar hydrogen generation by low-cost organic photoactive materials.