Discussion
In the ion implantation technique, nano-topography patterned surfaces are not concealed after implantation, and their efficacy in interacting with the osteoblasts is retained. Although all three studies examined the antibacterial effects of Ag2+ ions and the ability to promote bone tissue formation by MC3T3-E1 cells on SrHA-Ag/Ti surfaces, ion implantation techniques demonstrated superior ability. The synthesized specimen can be used as an effective implant in acetabular fracture sites based on their mechanical and biological properties.
Methods
A cylindrical Ti substrate mounted on a rotating specimen holder was used to implant Ca2+, P2+, and Sr2+ ions at energies of 100 KeV, 75 KeV and 180 KeV, respectively, using a low-energy accelerator to synthesize strontium-substituted hydroxyapatite at varying conditions. Ag2+ ions of energy 100 KeV were subsequently implanted on the as-formed surface at the near-surface region to provide anti-bacterial properties to the as-formed specimen.
Results
The properties of the as-formed ion-implanted specimen were compared with the SrHA-Ag synthesized specimens by cathodic deposition and low-temperature high-speed collision technique. The adhesion strength of the ion-implanted specimen was 43 ± 2.3 MPa, which is well above the ASTM standard for Ca-P coating on Ti. Live/dead cell analysis showed higher osteoblast activity on the ion-implanted specimen than the other two. Ag in the SrHA implanted Ti by ion implantation process showed superior antibacterial activity.