Abstract
To study the influence of brominated furanones on the biofilm (BF) formation by Escherichia coli (E. coli) on polyvinyl chloride (PVC) material, and to provide new ways of surface modification of materials to clinically prevent biomaterial centered infection. Three brominated furanones, dissolved in ethanol, furanone-1(3,4-dibromo-5-hydroxyl-furanone), furanone-2(4-bromo-5-(4-methoxypheny)-3-(methylamino)-furanone), and furanone-3(3,4-dibromo-5,5-dimethoxypheny-2(5H)-furanone) with representative chemical structure, were coated on the surfaces of separate PVC materials (1 × 1 cm), respectively. The surface-modified PVC materials were incubated with E. coli and for controls, 75 % ethanol-treated PVC materials were used. This treatment played as control group. The cultivation incubations were for 6, 12, 18, and 24 h. The thickness of bacterial BF and bacterial community quantity unit area on the PVC materials was determined by confocal laser scanning microscopy (CLSM), and the surface structure of bacterial BF formation was examined by scanning electron microscopy (SEM). The results of CLSM indicated the thickness of bacterial BF and bacterial community quantity unit area on PVC materials treated with furanone-3 were significantly lower than that of control at all time points (P < 0.05), whereas, the differences between furanone-1 and furanone-2 groups and control group were not significantly different (P > 0.05). The results of SEM indicated that after 6 h incubation, the quantity of bacterial attachment to the surface of PVC material treated with furanone-3 was lower than the control group. By 18 h incubation there was completely formed BF structure on the surface of control PVC material. However, there was no significant BF formation on the surface of PVC material treated with furanone-3. The impact of different brominated furanones on SA biofilm formation on the surface of PVC materials are different, furanone-3 can inhibit E. coli biofilm formation on the surface of PVC material.