Abstract
Nb, F-codoped TiO2 hollow spheres (NFTSs) were successfully synthesized via a hydrothermal method with niobium oxide, hydrofluoric acid, and tetrabutyl titanate. The obtained spheres were hollow, with a diameter of about 2 μm, and the sphere wall was made up of nanorods arranged close together. The NFTSs presented anatase phase with more {001} facets exposed, which could be mainly attributed to F ions which were preferentially adsorbed on the {001} facets during the crystal growth process. Ti3+ states in NFTSs were increased due to Nb, F-codoping, resulting in the decrease of the band gap and the red shift of the absorption edge of the NFTSs. The NFTSs exhibited 20.1% higher photocatalytic speed compared to P25 on the degradation of methylene orange.